304 stainless steel wire
chemical composition (%)
| C | Si | Mn | P | S | Ni | Cr |
| ≤0.07 | ≤1.00 | ≤2.00 | ≤0.035 | ≤0.03 | 8.00-11.00 | 17.00-19.00 |
physical property
| yield strength
σ0.2 (MPa) |
Tensile strength
σb (MPa) |
Elongation rate
δ5 (%) |
reduction of area
φ (%) |
Hard
HB |
Hard
HRB |
Hard
HV |
| ≥205 | ≥520 | ≥40 | ≥60 | ≤187 | ≤90 | ≤200 |
trademark
| CHINA
GB/T,YB |
US
ASTM |
Japan
JIS |
Germany
DIN EN |
UK
BS EN |
FRANCE
NF EN |
Russia
гOCT |
| 0Cr18Ni9 | 304 | SUS304 | X5CrNi18-10(1.4301) | 08X18H10 | ||
316 stainless steel wire
chemical composition (%)
| C | Si | Mn | P | S | Ni | Cr | Mo |
| ≤0.08 | ≤1.00 | ≤2.00 | ≤0.035 | ≤0.03 | 10.00-14.00 | 16.00-18.50 | 2.00-3.00 |
physical property
| yield strength
σ0.2 (MPa) |
Tensile strength
σb (MPa) |
Elongation rate
δ5 (%) |
reduction of area
φ (%) |
Hard
HB |
Hard
HRB |
Hard
HV |
| ≥205 | ≥520 | ≥40 | ≥60 | ≤187 | ≤90 | ≤200 |
trademark
| CHINA
GB/T,YB |
US
ASTM |
Japan
JIS |
Germany
DIN EN |
UK
BS EN |
FRANCE
NF EN |
Russia
гOCT |
| 0Cr17Ni12Mo2 | 316 | SUS316 | X5CrNiMo17-12-2(1.4401) | |||